钢包工作层用浇注料
The castables of The ladle working lining
刚玉尖晶石整体浇注料是以刚玉为主要原料，添加部份尖晶石或镁砂原料，以水泥或微粉为结合剂的不定形产品，使用中具有良好的整体性、抗侵蚀性及热震稳定性优的特点。
The corundum-spinel based castables is one integral casting refractory material of the ladle,using corundum as main material and incorporating certain spinel or magnesia materials,bound by the cement or micro-powder.This unshaped refractory has good integrity,excellent corrosion resistance and thermal shock stability.
| 项目 |
刚玉尖晶石浇注料 |
铝镁浇注料 |
刚玉自流料 |
高铝浇注料 |
| TCASS-6 |
TCASS-8 |
TAM-7-1AG |
TZLG-21 |
TZLG-3BT |
TBK-6T |
| 体积密度BD，g/cm3 |
110℃×24h |
3.15 |
3.10 |
3.00 |
3.10 |
2.80 |
2.60 |
| 耐压强度 MPa |
110℃×24h |
55.0 |
53.0 |
75.0 |
38.5 |
45.0 |
38.0 |
| 1550℃×3h |
165 |
177 |
110 |
120 |
102 |
80.3 |
抗折强度(Mpa) |
110℃×24h |
9.5 |
9.0 |
7.0 |
7.5 |
6.6 |
- |
| 1550℃×3h |
19.4 |
21.0 |
7.5 |
12.5 |
8.5 |
- |
残余线膨胀(%) |
1550℃×3h |
+0.12 |
+0.30 |
+0.50 |
+0.20 |
+0.10 |
+0.35 |
化学成份(%) |
Al2O3 |
93.30 |
92.70 |
75.00 |
88.50 |
17.50 |
66.50 |
| MgO |
3.20 |
3.50 |
10.00 |
- |
- |
- |
使用部份Application |
包壁 |
包底 |
包底 |
包底与包壁的缝隙 |
包嘴 |
钢包用腊石砖
Pyrophyllite brick for steel ladle –Introduction
以叶腊石为主要原料的烧成砖，在使用中具有一定的膨胀性，使用后整体性好，不粘渣。
项 目 |
PY-74 |
PY-80 |
| 显气孔率(%) |
≤15.5 |
≤15.5 |
| 体积密度BD，g/cm3 |
2.2 |
2.2 |
| 耐压强度 MPa |
36-41 |
41-45 |
| 耐火度(℃) |
1630 |
1650 |
化学成份(%) |
SiO2 |
≥74 |
≥80 |
| Fe2O3 |
≤0.5 |
≤0.5 |
| K2O+Na2O |
0.48 |
0.48 |
| Al2O3 |
≥15 |
≥13 |
铝碳化硅碳砖
提高钢包铁水包的使用寿命
该材料以优质特级矾土、叶腊石、碳化硅、碳原料结成，以高温树脂为结合剂大型压机成型生产，产品热震稳定性好，耐火度高，是钢包、铁水包用最优产品，可替代其他产品。
性 能 |
指标 |
| 显气孔率(%) |
15 |
| 体积密度kg/m3 |
2.3 |
| 耐压强度 MPa |
35 |
| 荷重软化温度(℃) |
1580 |
化学成份(%) |
SiC |
≥8 |
| SiO2 |
≥26 |
| AL2O3 |
≥40 |
| Fe3O2 |
<0.5 |